不锈钢(316L) |
||
| 物理特性 PHYSICAL CHARACTERISTICS |
||
| 粒径: |
15~53μm |
|
| 形态: |
球形 |
|
| 流动性: |
40S(霍尔流速计) |
|
| 松装密度： |
3.9 g/cm³ |
|
| 化学成分 CHEMICAL COMPOSITION |
||
| Fe: |
余量 |
|
| Cr: |
16~18% |
|
| Ni: |
10~14% |
|
| Mo: |
2~3% |
|
| Mn: |
≤2% |
|
| Si: |
≤1% |
|
| C: |
≤0.03% |
|
| P: |
≤0.0045% |
|
| S: |
≤0.03% |
|
| H: |
≤120ppm |
|
| O: |
≤0.13% |
|
| 成型件性能 MOLDING PERFORMANCE |
||
| 致密度: |
≥99% |
|
| 密度: |
7.98 g/cm³ |
|
| 抗拉强度: |
≥560 MPa |
|
| 屈服强度: |
≥480 MPa |
|
| 断裂伸长率: |
10~20 % |
|
| 弹性模量: |
180 GPa |
|
| 硬度: |
158 HB |
|
钛合金(TC4/Ti₆Al₄V) |
||
| 物理特性 PHYSICAL CHARACTERISTICS |
||
| 粒径: |
15~45μm |
|
| 形态: |
球形 |
|
| 流动性: |
45S(霍尔流速计) |
|
| 松装密度： |
2.5 g/cm³ |
|
| 化学成分 CHEMICAL COMPOSITION |
||
| Ti: |
余量 |
|
| Al: |
5~6.75% |
|
| V: |
3.5~4.5% |
|
| Fe: |
≤0.3% |
|
| C: |
≤0.1% |
|
| Si: |
≤0.12% |
|
| O: |
≤1300ppm |
|
| N: |
≤400ppm |
|
| H: |
≤120ppm |
|
| 其他: |
≤0.4% |
|
| 成型件性能 MOLDING PERFORMANCE |
||
| 致密度: |
≥99% |
|
| 密度: |
4.51 g/cm³ |
|
| 抗拉强度: |
≥1000 MPa |
|
| 屈服强度: |
≥900 MPa |
|
| 断裂伸长率: |
4~10 % |
|
| 弹性模量: |
100~120 GPa |
|
| 硬度: |
294 HB |
|
铝合金(AlSi₁₀Mg) |
||
| 物理特性 PHYSICAL CHARACTERISTICS |
||
| 粒径: |
15~53μm |
|
| 形态: |
球形 |
|
| 流动性: |
150S(霍尔流速计) |
|
| 松装密度： |
1.45 g/cm³ |
|
| 化学成分 CHEMICAL COMPOSITION |
||
| Al: |
余量 |
|
| Si: |
9~10% |
|
| Mg: |
0.2~0.45% |
|
| Cu: |
≤0.05% |
|
| Mn: |
≤0.45% |
|
| Ni: |
≤0.05% |
|
| Fe: |
≤0.55% |
|
| Ti: |
≤0.15% |
|
| O: |
≤0.15% |
|
| 成型件性能 MOLDING PERFORMANCE |
||
| 致密度: |
≥99% |
|
| 密度: |
2.67 g/cm³ |
|
| 抗拉强度: |
≥330 MPa |
|
| 屈服强度: |
≥245 MPa |
|
| 断裂伸长率: |
6 % |
|
| 弹性模量: |
70 GPa |
|
| 硬度: |
120 HB |
|